ingot700x150a
ALU-STOP LC15
• boron nitride coating for high performance
• for aluminium, magnesium, zinc and lead
• yields non-wetting, lubricating surfaces
• for ladles, troughs, dies, thermocouples, ingot moulds
• also available in colour for better contrast
• contains "white graphite"

Description

ALU-STOP LC15 Boron-Nitride-Coating is special coating for the non-ferrous metal casting and is characterised by a high content of boron nitride. Thus ALU-STOP LC15 Boron-Nitride-Coating shows a very good non-wetting behaviour against Al, Mg, Zn and Pb as well as their alloys. It is an ideal high temperature release and lubrication agent for the coating of ladles, troughs, distribution troughs, moulds and protects these efficiently against attacks by aggressive melts. The use of ALU-STOP LC15 Boron-Nitride-Coating on Wagstaff™ Casting Systems is described in its own data sheet. For highest performance the concentrate ALU-STOP LC25 Boron-Nitride-Coating is available. For standard applications the ready for use suspensions ALU-STOP LC10 Boron-Nitride-Coating and ALU-STOP LC5 Boron-Nitride-Coating are used.

Application

• Resuspend coating prior to use and dilute with distilled water if necessary.
• Application on clean surfaces is possible by painting or spraying. Best results may be achieved by spraying onto warm surfaces (50-150°C, 122-302°F).
• Dry thoroughly. Do not contact wet coatings with metal melts. Additional layers may be applied after drying.
• Best performance of ALU-STOP LC15 Boron-Nitride-Coating is achieved by thin coatings (up to 50-150µm). Thick coatings may crack during use.
• Do not damage coating during use because damaged areas are not sufficiently protected.
• Tools may be cleaned with water.

Storage-Container Size

ALU-STOP LC15 Boron-Nitride-Coating must be protected against frost. A storage temperature of >5°C (>41°F) is recommended. The containers should be kept closed. ALU-STOP LC15 Boron-Nitride-Coating is available in 6kg-containers.

Technical Data

Colour

white or coloured

Ceramic Constituent

Boron Nitride

Binder

Alumina

Solid Content (Boron Nitride)

15%

Density

1,15 g/cm³

Temperature (max. Application)

1000°C (at air)

1800°C (under inert gas)

 


© 2023 Büro für angewandte Mineralogie · Dr. Stephan Rudolph · D-47918 Tönisvorst


These recommendations are believed to be correct. However, no guarantee of their accuracy is given. Therefore, purchasers shall make their own tests to determine suitability for their use. These products are offered for industrial and related uses (e.g. research and development) only. However the user must take the necessary precautions appropriate for products containing chemicals. This description does not imply the absence of any patents, the responsibility whatsoever solely rests with the user.

alu-stop.com